Skip to main page content
U.S. flag

An official website of the United States government

Dot gov

The .gov means it’s official.
Federal government websites often end in .gov or .mil. Before sharing sensitive information, make sure you’re on a federal government site.

Https

The site is secure.
The https:// ensures that you are connecting to the official website and that any information you provide is encrypted and transmitted securely.

Access keys NCBI Homepage MyNCBI Homepage Main Content Main Navigation

Search Page

Filters

My NCBI Filters

Results by year

Table representation of search results timeline featuring number of search results per year.

Year Number of Results
2015 1
2016 1
2017 1
2024 0

Text availability

Article attribute

Article type

Publication date

Search Results

3 results

Results by year

Filters applied: . Clear all
Your search was processed without automatic term mapping because it retrieved zero results.
Page 1
Impact of machining on the flexural fatigue strength of glass and polycrystalline CAD/CAM ceramics.
Fraga S, Amaral M, Bottino MA, Valandro LF, Kleverlaan CJ, May LG. Fraga S, et al. Dent Mater. 2017 Nov;33(11):1286-1297. doi: 10.1016/j.dental.2017.07.019. Epub 2017 Aug 14. Dent Mater. 2017. PMID: 28818339
The greatest reduction in flexural fatigue strength from MP to M was observed for Y-TZP (40%; M=536.48MPa; MP=894.50MPa), followed by lithium disilicate (33%; M=187.71MPa; MP=278.93MPa) and leucite (29%; M=72.61MPa; MP=102.55MPa). Significantly higher …
The greatest reduction in flexural fatigue strength from MP to M was observed for Y-TZP (40%; M=536.48MPa; MP=894.50MPa), foll …
Extended glaze firing improves flexural strength of a glass ceramic.
Aurélio IL, Fraga S, Dorneles LS, Bottino MA, May LG. Aurélio IL, et al. Dent Mater. 2015 Dec;31(12):e316-24. doi: 10.1016/j.dental.2015.10.012. Dent Mater. 2015. PMID: 26599302
Regimens EF575-SC, G790-SC, and G790 produced sigma0 values (167.9, 157.7, and 153.7MPa, respectively) lower than the control (C) (187.7MPa). The Weibull modulus (m) was statistically similar between groups. All treatments reduced the mean roughness (Ra) of the specimens. …
Regimens EF575-SC, G790-SC, and G790 produced sigma0 values (167.9, 157.7, and 153.7MPa, respectively) lower than the control (C) (187.7MPa) …