Analysis of the degradation and crystallization behavior during the thermal degradation of poly(lactic acid)/modified hectorite nanocomposites films by simultaneous rheology and FTIR technology

Abstract

This study presents the synthesis of Hec-g@PS through the innovative surface modification of hectorite via photocatalytic atom transfer radical polymerization (ATRP). Then, PLA/Hec-g@PS nanocomposites films was prepared with Hec-g@PS as additives by blown molding technique. Furthermore, the thermal degradation kinetics and crystallization kinetics during the thermal degradation of PLA based nanocomposites films were investigated with simultaneous rheology and FTIR technology. The findings indicated that the activation energies for PLA and PLA/Hec-g@PS were -54,702.12 J/mol and -107,963.47 J/mol, respectively, demonstrating that Hec-g@PS substantially influenced PLA thermal stability. Additionally, while the crystallization rates of PLA based films decreased with rising degradation temperatures. Quantum chemical calculations revealed that the mode of interaction between Hec-g@PS and PLA was mainly dominated by dispersion, supplemented by electrostatic and induced interactions of -22.2103 kcal/mol, -16.0779 kcal/mol and -5.4954 kcal/mol, respectively. The combination of crystallization kinetics and quantum chemical calculations further confirmed that Hec-g@PS promoted the alignment of PLA molecular chains due to the enhanced interaction force between them. Hec-g@PS functioned as a nucleating agent, facilitating PLA crystallization and effectively mitigated its thermal degradation. Hec-g@PS as a nucleating agent provides valuable insights into the potential application prospects of biodegradable materials, particularly in the fields of biomedicine and packaging.

Keywords: Crystallization kinetics; Hectorite; Photocatalytic atom transfer radical polymerization; Poly(lactic acid); Thermal degradation.