Toxic organic dyes (colorants) are one of the main causes of water pollution that releases destructive effluents in the environment. To overcome this issue, a fundamental need to produce a novel, efficient catalyst for the degradation and mineralization of dye mixtures has arisen. The objective of this research is to develop an eminent Ni-doped magnetic carbon aerogel (Ni-MCA) catalyst using graft co-polymerization method having xanthan gum as backbone doped with Ni-magnetic nanoparticles (Ni-MNPs), that do not show agglomeration and easy to separate. The examination revealed that Ni-MCA provided exceptional magnetic characteristics (Ms = 52.75 emu/g) and potent catalytic activity for the degradation of mono- as well as binary-dye solutions of Congo red (CR) and methyl green (MG) dyes. The formation was verified by various characterization techniques such as FTIR, VSM, XRD, XPS, SEM, TEM, and EDX mapping. Interestingly, Ni-MCA shows faster result on anionic dye CR up to 97% with degradation rate of 5.647 × 10-1 min-1, and MG dye shows degradation of 95.7% with the degradation rate of 2.169 × 10-1 min-1, while dye mixture is showing 90% degradation with rate of 2.159 × 10-1 min-1.
Keywords: Binary dye degradation; Catalytic degradation; Magnetic carbon aerogel; Organic toxic dyes; Water treatment.
© 2024. The Author(s), under exclusive licence to Springer-Verlag GmbH Germany, part of Springer Nature.