Syngas produced from supercritical water gasification typically contain a high amount of CO2 along with H2. In order to improve the quality of syngas, amine-functionalized copper benzene-1,3,5-tricarboxylate (Cu-BTC) was synthesized as an effective adsorbent for selective removal of CO2 from syngas to increase the concentration of H2. The amines used in this study included monoethanolamine (MEA), ethylenediamine (EDA), and polyethyleneimine (PEI). The fundamental physicochemical character of adsorbents, CO2 adsorption capacity, and CO2/H2 selectivity were analyzed. The physicochemical characterization indicated that the structure of amine-functionalized Cu-BTC was partially damaged, which resulted in a decrease in specific surface area and pore volume. On the other hand, the enlarged pore size was beneficial for the mass transfer of gas in the adsorbent. Among these adsorbents, Cu-BTC/PEI exhibited the maximum CO2 adsorption capacity of 3.83 mmol/g and the highest CO2/H2 selectivity of 19.74. It was found that the adsorption pressure is the most significant factor for the CO2 adsorption capacity. Lower temperature and higher pressure were favored for CO2 adsorption capacity and CO2/H2 selectivity, so physical adsorption by Cu-BTC played a dominant role. Moreover, Cu-BTC/PEI can be well-regenerated with stable adsorption efficiency after five consecutive cycles. These findings suggested that Cu-BTC/PEI could be a promising alternative adsorbent for CO2 capture from syngas.
Keywords: Carbon capture; Metal–organic framework; Modification; Multi-component gas; Selectivity; Separation.
© 2024. The Author(s), under exclusive licence to Springer-Verlag GmbH Germany, part of Springer Nature.