Lignin is insoluble in water, thereby limiting its use in the synthesis of adhesives. Therefore, in this study, an aminated lignin compound was prepared through a lignin amination reaction to increase the amount of raw lignin material that can be used in the synthesis of adhesives; moreover, structural analysis was conducted. The main result of this was the introduction of amino groups into phenolic hydroxyl groups in the hydrolyzing lignin from the raw lignin materials, thus generating the product of aminated lignin. The resulting particle sizes were about 100 nm, the average molecular weight was 57,627 g/mol, and the water solubility of the aminated lignin was about 0.45 g/100 mL. Therefore, the water solubility of raw lignin was greatly improved. The proposed reaction mechanism of phenolic hydroxyl groups and carboxylic acid groups in lignin is a reaction with ammonia molecules; thus, the successful introduction of amino groups generated the aminated lignin compounds. Hence, this article enriches the scientific theory of lignin reactions and provides a reference for the widespread application of raw lignin materials in the field of adhesives.
Keywords: aminated lignin; ammonia; lignin.