Blends of polylactic acid (PLA) with amorphous polyhydroxyalkanoate (aPHA) are less brittle than neat PLA, thus enabling their use as biodegradable packaging. This work investigated the impact of recycling on the properties of neat PLA and PLA/aPHA blends with 90 and 75 wt. % PLA. After the materials were subjected to five heat histories in a single-screw extruder, the mechanical, rheological, and thermal properties were measured. All recycled compounds with 100% PLA and 75% PLA had similar decomposition behavior, whereas the decomposition temperatures for the blends with 90% PLA decreased with each additional heat cycle. The glass transition and melting temperatures were not impacted by reprocessing, but the crystallinity increased with more heat cycles. The complex viscosity of the reprocessed PLA and PLA/aPHA blends was much lower than for the neat PLA and increasing the number of heat cycles produced smaller reductions in the complex viscosity of 100% PLA and the blend with 90% PLA; no change in complex viscosity was observed for blends with 75% PLA exposed to 2 to 5 heat cycles. The tensile properties were not affected by reprocessing, whereas the impact strength for the 75% PLA blend decreased with reprocessing. These properties suggest that users will be able to incorporate scrap into the neat resin for thermoformed packaging.
Keywords: amorphous polyhydroxyalkanoate; biodegradable blends; polylactic acid.