A nano-structured conjugated polymer with multiple micro-/meso-pores was synthesized by post-crosslinking of an end-functionalized hyperbranched conjugated prepolymer. Firstly, an AB2 monomer 3-((3,5-dibromo-4-(octyloxy)phenyl)ethynyl)-6-ethynyl-9-octyl-9H-carbazole (PECz) was synthesized and polymerized by Sonogashira reaction to give the -Br end-functionalized hyperbranched conjugated prepolymer hb-PPECz. The photophysical and electrochemical properties of hb-PPECz were investigated. The λmax of absorption and emission of hb-PPECz in tetrahydrofuran (THF) solution was 313 and 483 nm, respectively. The optical energy bandgap, highest occupied molecular orbital (HOMO), and lowest unoccupied molecular orbital (LUMO) energy levels of hb-PPECz were 2.98, -5.81, and -2.83 eV, respectively. Then, the prepolymer hb-PPECz was post-crosslinked by Heck reaction with divinylbenzene to give the porous conjugated polymer c-PPECz. The effects of hb-PPECz concentration and added dispersant polyvinylpyrrolidone (PVP K-30) on the morphology and porosity of c-PPECz were investigated. The resulting c-PPECzs showed multiple porous structures mainly constructed by micropores and mesopores. Under a higher hb-PPECz concentration (4 wt/v%), a bulky gel product was obtained. Under lower hb-PPECz concentrations (0.6 wt/v%~2 wt/v%), the resulting c-PPECzs were mainly composed of nano-sized particles. Nearly spheric nanoparticles (200~300 nm) (c-PPECz-5) were obtained under the concentration of 1 wt/v% in the presence of PVP (10 wt% of hb-PPECz). The Brunauer-Emmett-Teller (BET) surface area, pore volume, average pore size, and percentage of pore size below 10 nm of c-PPECz-5 were 10.7781 m2·g-1, 0.0108 cm3·g-1, 4.0081 nm, and 94.47%, respectively.
Keywords: Heck reaction; Sonogashira coupling reaction; hyperbranched conjugated polymer; microporous conjugated polymer; post-crosslinking.