Duplex stainless steels are widely used in many fields due to their excellent corrosion resistance and mechanical properties. However, it is a challenge to achieve duplex microstructure and excellent properties through additive manufacturing. In this work, a 0.09% N 25Cr-type duplex stainless steel was prepared by additive manufacturing (AM) and heat treatment, and its corrosion resistance was investigated. The results show that, compared with S32750 duplex stainless steel prepared by a conventional process, the combination value of film resistance and charge transfer resistance of AM duplex stainless steel was increased by 3.2-5.5 times and the pitting potential was increased by more than 100 mV. The disappearance of residual thermal stress and the reasonable distribution of Cr and N elements in the two phases are the reasons for the improvement of the corrosion resistance of AM duplex stainless steel after heat treatment. In addition, the extremely high purity of AM duplex stainless steel with no visible inclusions resulted in a higher corrosion resistance exhibited at lower pitting-resistance-equivalent number values.
Keywords: additive manufacturing; corrosion resistance; duplex stainless steels; microstructure; nano-inclusion.