Multi-material additive manufacturing using heterogeneous powders as raw materials is one of the important development directions of metal additive manufacturing technology. The evaporation behavior of heterogeneous powders in the selective laser melting (SLM) process has a significant influence on the accuracy of chemical composition control and the quality of the final product. In this paper, the fusion process of Fe20Mn (80 wt.% Fe and 20 wt.% Mn) heterogeneous powder, Fe and Mn elemental powders, and Fe20Mn pre-alloyed powder is numerically simulated using FLOW-3D® software and partially validated through SLM experimental results. The morphology and the characteristics of the flow field and temperature field in the melt pool for four kinds of powder materials are analyzed. The influence of the elemental evaporation behavior of different powders on the mass loss of the Mn element is discussed. The results show that the excessive accumulation of heat increases the maximum temperature of the melt pool, thus increasing mass loss. The Fe20Mn heterogeneous powder has a wider heat-affected zone and a higher peak value of temperature, nearly 400 K higher than that of the Fe20Mn pre-alloyed powders, which exhibits an intensive evaporation behavior. The mass loss of the Mn element obtained from the SLM experiment for Fe20Mn heterogeneous powders forming parts is more than the Fe20Mn pre-alloyed powders' forming parts for different laser powers, up to 17 wt.% at P = 120 W. This tendency is consistent with the numerical analysis of the effect of evaporation behavior of Fe-Mn heterogeneous powder during the SLM process. This study provides the necessary theoretical reference and process guidance for realizing the precise control of the SLM composition of a heterogeneous powder in multi-material additive manufacturing caused by evaporation behavior.
Keywords: evaporation behavior; mass loss; multi-material additive manufacturing; numerical simulation; selective laser melting.