Thermal deformation behavior of Cu-Cr-Sn alloy ingots under deformation temperatures ranging from 600 °C to 950 °C and strain rates from 0.01 s-1 to 10 s-1 was investigated in detail. The thermal deformation constitutive equation and thermal processing map of the alloy were established, respectively. The activation energy Q was determined as 430.61 KJ/mol. The optimal deformation system corresponding to the hot working diagram was a deformation temperature of 900 °C and strain rate of 0.1 s-1. Under these deformation conditions, twin dynamic recrystallization (TDRX), continuous dynamic recrystallization (CDRX), and discontinuous dynamic recrystallization (DDRX) occurred simultaneously, with the twinning process causing the stress-strain curve to exhibit a wavy change. The thermal deformation microstructure of the alloy is co-regulated by different recrystallization mechanisms, with DDRX occurring mainly at low deformation temperatures, and both CDRX and DDRX occurring at high deformation temperatures.
Keywords: Cu–Cr–Sn alloy; constitutive model; microstructural evolution; softening mechanism; thermal deformation behavior.