This paper investigates the impact of varying the part geometric complexity and 3D printing process setup on the resulting structural load bearing capacity of fiber composites. Three levels of geometric complexity are developed through 2.5D topology optimization, 3D topology optimization, and 3D topology optimization with directional material removal. The 3D topology optimization is performed with the SIMP method and accelerated by high-performance computing. The directional material removal is realized by incorporating the advection-diffusion partial differential equation-based filter to prevent interior void or undercut in certain directions. A set of 3D printing and mechanical performance tests are performed. It is interestingly found that, the printing direction affects significantly on the result performance and if subject to the uni direction, the load-bearing capacity increases from the 2.5D samples to the 3D samples with the increased complexity, but the load-bearing capacity further increases for the 3D simplified samples due to directional material removal. Hence, it is concluded that a restricted structural complexity is suitable for topology optimization of 3D-printed fiber composites, since large area cross-sections give more degrees of design freedom to the fiber path layout and also makes the inter-layer bond of the filaments firmer.
Keywords: 3D printing; fiber composites; geometric complexity; topology optimization.