Polypyrrole (PPy)-capped silver nanowire (Ag NW) nanomaterials (core-shell rod-shaped Ag NW@PPy) were synthesized using a one-port suspension polymerization technique. The thickness of the PPy layer on the 50 nm thickness/15 μm length Ag NW was effectively controlled to 10, 40, 50, and 60 nm. Thin films cast from one-dimensional conductive Ag NW@PPy formed a three-dimensional (3D) conductive porous network structure and provided excellent electrochemical performance. The 3D Ag NW@PPy network can significantly reduce the internal resistance of the electrode and maintain structural stability. As a result, a high specific capacitance of 625 F/g at a scan rate of 1 mV/s was obtained from the 3D porous Ag NW@PPy composite film. The cycling performance over a long period exceeding 10,000 cycles was also evaluated. We expect that our core-shell-structured Ag NW@PPy composites and their 3D porous structure network films can be applied as electrochemical materials for the design and manufacturing of supercapacitors and other energy storage devices.
Keywords: core–shell structure; nanorods; silver nanowire–polypyrrole composite; supercapacitor.