Purpose This study evaluated the color alterations, flexural strength and microhardness properties of two different 3D-printed permanent crown resins. Materials and Methods Samples were produced from two different 3D Print permanent crown resins: Group 1 (Saremco Crowntec; Saremco, Switzerland), Group 2 (P-crown Version 2; Senertek, Turkey). Color changes (ΔE values), flexural strenght and vickers hardness number of the samples were calculated. Data were analyzed with Shapiro-Wilk normality test, Independent-t test, and Mann Whitney-U tests. Significance level was accepted as P<0.05. Results ΔE values for red wine were found to be significantly higher in Group 1 (6.43Å}2.26; P<0.001). The flexural strength values (MPa) of Group 1 were significantly higher than Group 2 in all three solutions (P<0.001). There was no significant difference between the VHN values of the samples kept in wine and coffee solutions (P= 0.271; 0.827). Conclusion 3D printing resins are affected at different levels by coloring solutions. Microhardness and flexural strength of 3D print samples kept in different coloring agents are different.In the use of 3D printing resins, product selection should be made by taking into account the individual factors such as the eating and drinking habits of the patients and the physical properties expected from the sample.
Keywords: 3D Printing; Color Alterations; Flexural Strength; Permanent Crown Resin; Vickers Hardness Test..