The research presented in this article focuses on the use of inorganic-organic material, based on titanium dioxide and lignin, as a filler for polylactide (PLA) biocomposites. To date, no research has been conducted to understand the impact of hybrid fillers consisting of TiO2 and lignin on the supermolecular structure and crystallization abilities of polylactide. Polymer composites containing 1, 3 or 5 wt.% of hybrid filler or TiO2 were assessed in terms of their structure, morphology, and thermal properties. Mechanical properties, including tensile testing, bending, impact strength, and hardness, were discussed. The hybrid filler is characterized by a very good electrokinetic stability at pH greater than 3-4. The addition of all fillers led to a small decrease in the glass transition temperature but, most importantly, the addition of 1% of the hybrid filler to the PLA matrix increased the degree of crystallinity of the material by up to 20%. Microscopic studies revealed differences in the crystallization behavior and nucleation ability of fillers. The use of hybrid filler resulted in higher nucleation density and shorter induction time than in unfilled PLA or PLA with only TiO2. The introduction of small amounts of hybrid filler also affected the mechanical properties of the composites, causing an increase in bending strength and hardness. This information may be useful from a technological process standpoint and may also help to increase the range of applicability of biobased materials.
Keywords: TiO2; biocomposites; hybrid materials; lignin; polylactide.