Contact resistance, as one of the main parameters that limits the performance of graphene-based transistors, is highly dependent on the metal-graphene contact fabrication processes. These processes are investigated and the corresponding resistances are measured based on the transfer length method (TLM). In fabrication processes, when annealing is done on chemical vapor deposition (CVD)-grown graphene samples that are transferred onto SiO2/Si substrates, the adhesion of graphene to the substrate is improved, and poly methyl methacrylate (PMMA) residues are also reduced. When the metal deposition layer is first applied to the graphene, and then, the photolithography process is performed to define the electrodes and graphene sheet, the graphene-metal contact resistance is better than that in other methods due to the removal of photoresist residues. In fact, by changing the sequence of the fabrication process steps, the direct contact between photoresist and graphene surface can be prevented. Thus, the contact resistance is reduced and conductivity increases, and in this way, the performance of graphene transistor improves. The results show that the fabrication process has a noticeable effect on the transistor properties such as contact resistance, channel sheet resistance, and conductivity. Here, by using the annealing process and changing the order of photolithography processes, a contact resistance of 470 Ω μm is obtained for Ni-graphene contact, which is relatively favorable.
© 2024. The Author(s).