Magnetic refrigeration technology can achieve higher energy efficiency based on the magnetocaloric effect (MCE). However, the practical application of MCE materials is hindered by their poor mechanical properties, making them challenging to process into devices. Conventional strengthening strategies usually lead to a trade-off with refrigeration capacity reduction. Here, a novel design is presented to overcome this dilemma by forming dual-phase alloys through in situ precipitation of a tough magnetic refrigeration phase within an intermetallic compound with excellent MCE. In the alloy 87.5Gd-12.5Co, incorporating the interconnected tough phase Gd contributes to enhanced strength (≈505 MPa) with good ductility (≈9.2%). The strengthening phase Gd simultaneously exhibits excellent MCE, enabling the alloy to achieve a peak refrigeration capacity of 720 J kg-1. Moreover, the alloy shows low thermal expansion induced by the synergistic effect of the two phases. It is beneficial for maintaining structural stability during heat exchange in magnetic refrigeration. The coupling interaction between the two magnetic phases can broaden the refrigeration temperature range and reduce hysteresis. This study guides the development of new high-performance materials with an excellent combination of mechanical and magnetic refrigeration properties as needed for gas liquefaction and refrigerators.
Keywords: dual‐phase alloy; magnetocaloric materials; mechanical performances; refrigeration capacity.
© 2024 Wiley‐VCH GmbH.