FeNbO4 sonocatalysts were successfully synthesized by a simple hydrothermal route at pH values of 3, 5, 7, 9 and 11. The catalysts were characterized by XRD, XPS, TEM, SEM, N2 adsorption and DRS to analyse the effect of pH parameters on the physicochemical properties of the materials during hydrothermal synthesis. The sonocatalytic activity of FeNbO4 microspheres was evaluated by using acid orange 7 (AO7) as the simulated contaminant. The experimental results showed that the best sonocatalytic degradation ratio (97.45%) of organic dyes could be obtained under the conditions of an initial AO7 concentration of 10 mg L-1, an ultrasonic power of 200 W, a catalyst dosage of 1.0 g L-1, and a pH of 3. Moreover, the sonocatalysts demonstrated consistent durability and stability across multiple test cycles. After active species capture experiments and calculation of the energy band, a possible mechanism was proposed based on the special Fenton-like mechanism and the dissociation of H2O2. This research shows that FeNbO4 microspheres can be used as sonocatalysts for the purification of organic wastewater, which has a promising application prospect.
This journal is © The Royal Society of Chemistry and the Centre National de la Recherche Scientifique.