The accumulation of ice can pose numerous inconveniences and potential hazards, profoundly affecting both human productivity and daily life. To combat the challenges posed by icing, extensive research efforts have been dedicated to the development of low-ice adhesion surfaces. In this study, we harness the power of molecular dynamics simulations to delve into the intricate dynamics of polymer chains and their role in determining the modulus of the material. We present a novel strategy to prepare ultralow-modulus poly(dimethylsiloxane) (PDMS) elastomers with a molecular brush configuration as icephobic materials. The process involves grafting monohydride-terminated PDMS (H-PDMS) as side chains onto backbone chain PDMS with pendant vinyl functional groups to yield a molecular brush structure. The segments of this polymer structure effectively restrict interchain entanglement, thereby rendering a lower modulus compared to traditional linear structures at an equivalent cross-linking density. The developed soft coating exhibits a remarkably ultralow ice adhesion strength of 13.1 ± 1.1 kPa. Even after enduring 50 cycles of icing and deicing, the ice adhesion strength of this coating steadfastly stayed below 16 kPa, showing no notable increase. Importantly, the molecular brush coating applied to glass demonstrated an impressive light transmittance of 92.1% within the visible light spectrum, surpassing the transmittance of bare glass, which was measured at 91.3%. This icephobic coating with exceptional light transmittance offers a wide range of applications and holds significant potential as a practical icephobic material.
Keywords: ice adhesion strength; icephobic coating; lower modulus; molecular brush; molecular dynamics.