Porous anorthite (CaAl2Si2O8) ceramics, suitable for thermal insulation in buildings, were obtained using waste seashells as a source of CaO, kaolin as a source of Al2O3 and SiO2 and banana peel as a pore former. Changing the volume of banana peel as well as the processing temperature was found to be an effective approach to control the thermo-mechanical properties of the obtained anorthite ceramics. The sintering of powder compacts containing up to 30 wt% banana peel at temperatures ranging from 1100 to 1200 °C resulted in anorthite ceramics possessing up to 45% open porosity, a compressive strength between 13 and 92 MPa, a bulk density between 1.87 and 2.62 g/cm3 and thermal conductivity between 0.097 and 3.5 W/mK. It was shown that waste materials such as seashells and banana peel can be used to obtain cost-effective thermal insulation in buildings.
Keywords: anorthite; banana peel; microstructure; porous ceramics; thermo-mechanical properties; waste seashells.