The failure mechanism of thermal gate oxide in silicon carbide (SiC) power metal oxide semiconductor field effect transistors (MOSFETs), whether it is field-driven breakdown or charge-driven breakdown, has always been a controversial topic. Previous studies have demonstrated that the failure time of thermally grown silicon dioxide (SiO2) on SiC stressed with a constant voltage is indicated as charge driven rather than field driven through the observation of Weibull Slope β. Considering the importance of the accurate failure mechanism for the thermal gate oxide lifetime prediction model of time-dependent dielectric breakdown (TDDB), charge-driven breakdown needs to be further fundamentally justified. In this work, the charge-to-breakdown (QBD) of the thermal gate oxide in a type of commercial planar SiC power MOSFETs, under the constant current stress (CCS), constant voltage stress (CVS), and pulsed voltage stress (PVS) are extracted, respectively. A mathematical electron trapping model in thermal SiO2 grown on single crystal silicon (Si) under CCS, which was proposed by M. Liang et al., is proven to work equally well with thermal SiO2 grown on SiC and used to deduce the QBD model of the device under test (DUT). Compared with the QBD obtained under the three stress conditions, the charge-driven breakdown mechanism is validated in the thermal gate oxide of SiC power MOSFETs.
Keywords: CCS; CVS; MOSFET; PVS; QBD; SiC; charge-driven breakdown; electron trapping model; thermal gate oxide.