Liquid silicone rubber (LSR) garners attention across a diverse range of industries owing to its commendable fluidity and heat resistance. Nonetheless, its mechanical strength and oil resistance fall short compared to other rubbers, necessitating enhancement through the incorporation of a suitable filler. This research focuses on reinforcing LSR using carbon black (CB) particles as a filler, evaluating the mechanical properties and oil resistance of neat LSR, and LSR containing up to 3 wt% of CB filler. CB was added in powder form to investigate its effect on LSR. When LSR was impregnated with oil, the deterioration of rubber was noticeably observed under high-temperature conditions compared to room-temperature conditions. Consequently, the mechanical properties and oil resistance, excluding the permanent compression reduction rate, tended to increase as the filling content of CB increased compared to the unfilled state. Notably, in the specimen with 2 wt% CB filler, the tensile modulus increased significantly by 48% and the deterioration rate was reduced by about 50% under accelerated deterioration conditions. Additionally, the swelling rate in oil decreased by around 14%. This validates a notable improvement in both mechanical properties and oil resistance. Based on the identified mechanism for properties enhancement in this study, CB/LSR composite is expected to have a wide range of applications in fields such as gaskets, oil seals, and flexible sensors.
Keywords: carbon black; liquid silicone rubber; mechanical properties; oil resistance; swelling.