Nanoparticles of MgSb2O6 were synthesized using a microwave-assisted wet chemistry method, followed by calcination at 700 °C. Their ability to detect different concentrations of propane gas (C3H8) at various operating voltages was evaluated. The material's crystalline phase was identified using X-ray powder diffraction (XRD). The morphology was analyzed by scanning electron microscopy (SEM), finding bar- and polyhedron-type geometries. Through transmission electron microscopy (TEM), we found particle sizes of 8.87-99.85 nm with an average of ~27.63 nm. Employing ultraviolet-visible (UV-Vis) spectroscopy, we found a band gap value of ~3.86 eV. Thick films made with MgSb2O6 powders were exposed to atmospheres containing 150, 300, 400, and 600 ppm of propane gas for dynamic testing. The time-dependent sensitivities were ~61.09, ~88.80, ~97.65, and ~112.81%. In addition, tests were carried out at different operating voltages (5-50 V), finding very short response and recovery times (~57.25 and ~18.45 s, respectively) at 50 V. The excellent dynamic response of the MgSb2O6 is attributed mainly to the synthesis method because it was possible to obtain nanometric-sized particles. Our results show that the trirutile-type oxide MgSb2O6 possesses the ability, efficiency, and thermal stability to be applied as a gas sensor for propane.
Keywords: MgSb2O6; gas sensor; sensitivity; thick films.