Lithium (Li) metal is widely recognized as a viable candidate for anode material in future battery technologies due to its exceptional energy density. Nevertheless, the commercial Li foils in common use are too thick (≈100 µm), resulting in a waste of Li resources. Herein, by applying the vacuum evaporation plating technology, the ultra-thin Li foils (VELi) with high purity, strong adhesion, and thickness of less than 10 µm are successfully prepared. The manipulation of evaporation temperature allows for convenient regulation of the thickness of the fabricated Li film. This physical thinning method allows for fast, continuous, and highly accurate mass production. With a current density of 0.5 mA cm-2 for a plating amount of 0.5 mAh cm-2, VELi||VELi cells can stably cycle for 200 h. The maximum utilization of Li is already more than 25%. Furthermore, LiFePO4||VELi full cells present excellent cycling performance at 1 C (1 C = 155 mAh g-1) with a capacity retention rate of 90.56% after 240 cycles. VELi increases the utilization of active Li and significantly reduces the cost of Li usage while ensuring anode cycling and multiplication performance. Vacuum evaporation plating technology provides a feasible strategy for the practical application of ultra-thin Li anodes.
Keywords: lithium metal battery; ultrathin lithium anode; vacuum evaporation plating.
© 2024 Wiley‐VCH GmbH.