Fe-based Prussian blue (Fe-PB) analogues have emerged as promising cathode materials for sodium-ion batteries, owing to their cost-effectiveness, high theoretical capacity, and environmental friendliness. However, their practical application is hindered by [Fe(CN)6] defects, negatively impacting capacity and cycle stability. This work reports a hollow layered Fe-PB composite material using 1,3,5-benzenetricarboxylic acid (BTA) as a chelating and etching agent by the hydrothermal method. Compared to benzoic acid, our approach significantly reduces defects and enhances the yield of Fe-PB. Notably, the hollow layered structure shortens the diffusion path of sodium ions, enhances the activity of low-spin Fe in the Fe-PB lattice, and mitigates volume changes during Na-ion insertion/extraction into/from Fe-PB. As a sodium-ion battery cathode, this hollow layered Fe-PB exhibits an impressive initial capacity of 95.9 mAh g-1 at a high current density of 1 A g-1. Even after 500 cycles, it still maintains a considerable discharge capacity of 73.1 mAh g-1, showing a significantly lower capacity decay rate (0.048%) compared to the control sample (0.089%). Moreover, the full cell with BTA-PB-1.6 as the cathode and HC as the anode provides a considerable energy density of 312.2 Wh kg-1 at a power density of 291.0 W kg-1. This research not only enhances the Na storage performance of Fe-PB but also increases the yield of products obtained by hydrothermal methods, providing some technical reference for the production of PB materials using the low-yield hydrothermal method.
Keywords: 1,3,5-benzenetricarboxylic acid; Prussian blue analogues; cathode material; hollow layered structure; hydrothermal method; sodium-ion battery.