(K0.5Na0.5)NbO3 (KNN)-based ceramics have been extensively investigated as replacements for Pb(Zr, Ti)O3-based ceramics. KNN-based ceramics exhibit an orthorhombic structure at room temperature and a rhombohedral-orthorhombic (R-O) phase transition temperature (TR-O), orthorhombic-tetragonal (O-T) phase transition temperature (TO-T), and Curie temperature of -110, 190, and 420 °C, respectively. Forming KNN-based ceramics with a multistructure that can assist in domain rotation is one technique for enhancing their piezoelectric properties. This review investigates and introduces KNN-based ceramics with various multistructures. A reactive-templated grain growth method that aligns the grains of piezoceramics in a specific orientation is another approach for improving the piezoelectric properties of KNN-modified ceramics. The piezoelectric properties of the [001]-textured KNN-based ceramics are improved because their microstructures are similar to those of the [001]-oriented single crystals. The improvement in the piezoelectric properties after [001] texturing is largely influenced by the crystal structure of the textured ceramics. In this review, [001]-textured KNN-based ceramics with different crystal structures are investigated and systematically summarized.
Keywords: KNN-based piezoceramic; lead-free; phase transition; polymorphic phase boundary; reactive template grain growth.