The data presented here aim to show how to analyze crack propagation of a novel metallic matrix composite of Ti-6Al-4V reinforced with 1 wt.% nano-yttria-stabilized zirconia processed by laser powder bed fusion technology. The data was acquired via microstructural observations and electron backscatter diffraction (EBSD) analyses after the quasistatic tensile tests at room temperature. The overall crack path configuration based on the fracture surface observation by scanning electron microscopy (SEM) was first operated, presenting two main regions: (i) local inclined planes (hereafter denoted as "stair-like"), and (ii) region in accordance with the theoretical mode I fracture plane. Thereafter, a series of EBSD data set on a surface obtained after longitudinal cut off operation on one failed piece was conducted at three distinct positions: (i) in the stair-like configuration region, (ii) in the mode I fracture region, and (iii) in the region where the crack path made his transition between these two mechanisms. Since the EBSD data sets were not prone to any post-processing filtering operation, comparison of the observed mechanism with other Ti-6Al-4V alloy processed by additive manufacturing (AM) technology can be easily carried out.
Keywords: Crack growth; EBSD characterization; Metal matrix composite; Rupture mechanism.
© 2024 The Authors. Published by Elsevier Inc.