Sodium foil, promising for high-energy-density batteries, faces reversibility challenges due to its inherent reactivity and unstable solid electrolyte interphase (SEI) layer. In this study, a stable sodium metal battery (SMB) is achieved by tuning the electrolyte solvation structure through the addition of co-solvent 2-methyl tetrahydrofuran (MTHF) to diglyme (Dig). The introduction of cyclic ether-based MTHF results in increased anion incorporation in the solvation structure, even at lower salt concentrations. Specifically, the anion stabilization capabilities of the environmentally sustainable MTHF co-solvent lead to a contact-ion pair-based solvation structure. Time-of-flight mass spectroscopy analysis reveals that a shift toward an anion-dominated solvation structure promotes the formation of a thin and uniform SEI layer. Consequently, employing a NaPF6-based electrolyte with a Dig:MTHF ratio of 50% (v/v) binary solvent yields an average Coulombic efficiency of 99.72% for 300 cycles in Cu||Na cell cycling. Remarkably, at a C/2 cycling rate, Na||Na symmetric cell cycling demonstrates ultra-long-term stability exceeding 7000 h, and full cells with Na0.44MnO2 as a cathode retain 80% of their capacity after 500 cycles. This study systematically examines solvation structure, SEI layer composition, and electrochemical cycling, emphasizing the significance of MTHF-based binary solvent mixtures for high-performance SMBs.
Keywords: electrolyte; long‐term stability; sodium metal batteries; solvation structure; solvent mixtures.
© 2024 Wiley‐VCH GmbH.