Sonochemical synthesis of CoNi layered double hydroxide as a cathode material for assembling high performance hybrid supercapacitor

Abstract

Fabricating battery-type electrode materials with large specific surface area and mesopores is an efficient method for enhancing the electrochemical performance of supercapacitors. This method may provide more active sites for Faradic reactions and shorten the ion-diffusion paths. In this study, the CoNi layered double hydroxides (LDHs) with the morphology of nanoflowers and nanoflakes were prepared in solutions with pH values of 7.5 (CoNi LDH-7.5) and 8.5 (CoNi LDH-8.5) via a simple sonochemical approach. These CoNi LDHs possessed large specific surface areas and favourable electrochemical properties. The CoNi LDH-7.5 delivered a specific capacity of 740.8C/g at a current density of 1 A/g, surpassing CoNi LDH-8.5 with 668.1C/g. The hybrid supercapacitor (HSC) was assembled with activated carbon as the anode and CoNi LDH as the cathode to assess its practical application potential in the field of electrochemical energy storage. The CoNi LDH-7.5//AC HSC achieved the highest energy density of 35.6 W h kg^-1 at a power density of 781.1 W kg^-1. In addition, both HSCs exhibited little capacity decay over 5,000 cycles at a high current load of 8 A/g. These electrochemical properties of CoNi LDHs make them promising candidates for battery-type electrode materials. The current sonochemical method is simple and can be applied to the preparation of other LDHs-based electrode materials with favourable electrochemical performance.

Keywords: CoNi LDHs; Electrochemical energy storage; Sonochemical synthesis; Supercapacitors.