Monodispersed microspheres play a major role in optical science and engineering, providing ideal building blocks for structural color materials. However, the method toward high solid content (HSC) monodispersed microspheres has remained a key hurdle. Herein, a facile access to harvest monodispersed microspheres based on the emulsion polymerization mechanism is demonstrated, where anionic and nonionic surfactants are employed to achieve the electrostatic and steric dual-stabilization balance in a synergistic manner. Monodispersed poly(styrene-butyl acrylate-methacrylic acid) colloidal latex with 55 wt% HSC is achieved, which shows an enhanced self-assembly efficiency of 280% compared with the low solid content (10 wt%) latex. In addition, Ag-coated colloidal photonic crystal (Ag@CPC) coating with near-zero refractive index is achieved, presenting the characteristics of metamaterials. And an 11-fold photoluminescence emission enhancement of CdSe@ZnS quantum dots is realized by the Ag@CPC metamaterial coating. Taking advantage of high assembly efficiency, easily large-scale film-forming of the 55 wt% HSC microspheres latex, robust Ag@CPC metamaterial coatings could be easily produced for passive cooling. The coating demonstrates excellent thermal insulation performance with theoretical cooling power of 30.4 W m-2, providing practical significance for scalable CPC architecture coatings in passive cooling.
Keywords: colloidal photonic crystals; high solid content; metamaterial; monodispersed microsphere; passive cooling.
© 2024 Wiley‐VCH GmbH.