Hitherto unreported hybrid nanofillers (CNC:MgO) reinforced chitosan (CTS) based composite (CNC:MgO)/CTS films were synthesized using a solution-casting blend technique and synergistic effect of hybrid nanofiller in terms of properties enhancement were investigated. Optical microscopy, transmission electron microscopy (TEM), X-ray diffraction (XRD) technique, fourier-transform infrared spectroscopy (FTIR), and field emission scanning electron microscopy (FESEM) were used to characterize the films. The hybrid nanofiller considerably changed the transparency and color of the CTS films. The tensile strengths of (3 wt%) CNC/CTS, (3 wt%) MgO/CTS, (1:1)(CNC:MgO)/CTS, (1:2)(CNC:MgO)/CTS and (2:1)(CNC:MgO)/CTS films were 27.49 %, 35.60 %, 91.62 %, 38.22 %, and 29.32 % higher than pristine CTS films respectively, while the water vapor permeation were 28.21 %, 30.77 %, 34.62 %, 38.46 %, and 37.44 % lower than pristine CTS film, respectively. Moreover, the CTS composite films exhibited an improvement in overall water barrier properties after incorporating hybrid nanofillers. Our observations suggest that chitosan-based hybrid nanofiller composite films are a good replacement for plastic-based packaging materials within the food industry.
Keywords: Cellulose nanocrystal; Chitosan; Magnesium oxide; Mechanical property; X-ray diffraction.
Copyright © 2024 Elsevier B.V. All rights reserved.