Aqueous MXene dispersion suffers from a bottleneck issue of oxidation, leading to its gradual deterioration and ultimately compromised physicochemical characteristics. Herein, Tris-HCl buffer is employed to stabilize the diluted Ti3 C2 Tx -MXene dispersion (0.05 mg mL-1 ) through the synergy of its potent pH-regulation capability and capping effect toward oxidation-susceptible defects/edges. Tris-HCl functionalized Ti3 C2 Tx maintained its original morphology, structure, and favorable dispersity even after 150 days of aging under naturally aerated conditions. The pH-regulation nature of Tris-HCl is elucidated through solution monitoring of Ti3 C2 Tx dispersion, while the adsorption of Tris-HCl onto defects/edges is revealed by spectral analysis and multi-scale simulations. Tris-HCl at the neutral pH can bind to the negatively charged basal plane of Ti3 C2 Tx via + HTris moiety, while the other moiety (Tris) interacts with the exposed edge-based Ti atoms and/or intrinsic defects, forming a Ti─N bond that prevents MXene from attack by H2 O and O2 . Besides, Tris-HCl stabilized Ti3 C2 Tx exhibited nearly identical capacitive characteristics to its freshly-etched counterpart, indicating the minimal impact of Tris-HCl on electrochemical performance of Ti3 C2 Tx during long-term storage. This study provides practical guidance for stabilizing MXene in their native aqueous dispersion without compromising the inherent properties.
Keywords: 2D MXene; Tris-HCl buffering; antioxidant; oxidation stability.
© 2024 Wiley-VCH GmbH.