Microstructural and micromechanical characteristics of composite osteoconductive coatings deposited by the atmospheric pressure plasma technique

Lukasz Major; D F Kopp; R Major; Jürgen Markus Lackner

doi:10.1111/jmi.13285

Microstructural and micromechanical characteristics of composite osteoconductive coatings deposited by the atmospheric pressure plasma technique

J Microsc. 2024 Feb 28. doi: 10.1111/jmi.13285. Online ahead of print.

Authors

Lukasz Major¹, D F Kopp², R Major¹, Jürgen Markus Lackner²

Affiliations

¹ Institute of Metallurgy and Materials Science, Polish Academy of Sciences, Cracow, Poland.
² JOANNEUM RESEARCH Forschungsgesellschaft m.b.H., Institute for Photonics, Sensorics and Manufacturing Technologies, Research Group Laser and Plasma Processing, Niklasdorf, Austria.

PMID: 38415368
DOI: 10.1111/jmi.13285

Abstract

Long-term placement of facial implants requires avoiding the formation of fibrous tissue capsules around the artificial material by creating osteoconductive properties of the surface. Most promising approach is the deposition coatings made of materials very similar to bone mineral components, that is, calcium phosphates such as hydroxyapatite (HAp). As part of the research work, an innovative, cost-effective atmospheric pressure plasma deposition (APPD) system was used as a low-temperature coating technology for generating the HAp coatings deposition. Full microstructural characterisation of the coatings using SEM and TEM techniques was carried out in the work. It has been shown that the fully crystalline HAp powder undergoes a transformation during the coatings deposition and the material had a quasi-sintered structure after deposition. The crystalline phase content increased at the coating/substrate interface, while the surface of the HAp was amorphous. This is a very beneficial phenomenon due to the process of bioresorption. The amorphous phase undergoes much faster biodegradation than the crystalline one. In order to increase the bioactivity of the HAp, Zn particles were introduced on the surface of the coating. The TEM microstructural analysis in conjunction with the qualitative analysis of the EDS chemical composition showed that the binding of the Zn particles within the HAp matrix had diffusive character, which is very favourable from the point of view of the quality of the adhesion and the bioactivity of the coating. In the case of such a complex structure and due to its very porous nature, micromechanical analysis was carried out in situ in SEM, that is, by microhardness measurements of both the HAp matrix and the Zn particle. It was shown that the average value of HAp microhardness was 4.395 GPa ± 0.08, while the average value of Zn microhardness was 1.142 GPa ± 0.02.

Keywords: HAp coatings; SEM; TEM; atmospheric pressure plasma deposition; in situ analysis in SEM; microstructure.