The melt-blowing process involves high velocity airflow and fiber motion, which have a significant effect on fiber attenuation. In this paper, the three-dimensional airflow field for a melt-blowing slot die was measured using the hot-wire anemometry in an experiment. The fiber motion was captured online using a high-speed camera. The characteristics of the airflow distribution and fiber motion were analyzed. The results show that the melt-blowing airflow field is asymmetrically distributed. The centerline air velocity is higher than that around it and decays quickly. The maximum airflow velocity exists near the die face, in the range of 130-160 m/s. In the region of -0.3 cm < y < 0.3 cm and 0 < z < 2 cm, the airflow has a high velocity (>100 m/s). As the distance of z reaches 5 cm and 7 cm, the maximum airflow velocity reduces to 70 m/s. The amplitude of fibers is calculated, and it increases with the increase in air dispersion area which has a significant influence on fiber attenuation. At z = 1.5 cm, 2.5 cm, 4 cm, and 5.5 cm, the average fiber amplitudes are 1.05 mm, 1.71 mm, 2.83 mm, and 3.97 mm, respectively. In the vicinity of the die, the fibers move vertically downward as straight segments. With the increase in distance from the spinneret, the fiber appears to bend significantly and forms a fiber loop. The fiber loop morphology affects the velocity of the fiber movement, causing crossover, folding, and bonding of the moving fiber. The study investigated the interaction between the fiber and airflow fields. It indicates that the airflow velocity, velocity difference, and dispersion area can affect the motion of fiber which plays an important role in fiber attenuation during the melt-blowing process.
Keywords: airflow field distribution; experimental measurement; fiber motion; melt blowing.