Mn-based magnets are known to be a candidate for use as rare-earth-free magnets. In this study, Mn-Ga bulk magnets were successfully produced by hot pressing using the spark plasma sintering method on Mn-Ga powder prepared from rapidly solidified Mn-Ga melt-spun ribbons. When consolidated at 773 K and 873 K, the Mn-Ga bulk magnets had fine grains and exhibited high coercivity values. The origin of the high coercivity of the Mn-Ga bulk magnets was the existence of the D022 phase. The Mn-Ga bulk magnet consolidated at 873 K exhibited the highest coercivity of 6.40 kOe.
Keywords: Mn-Ga alloys; coercivity; melt spinning; spark plasma sintering.