Rigid pavements at military airfields experience surface deterioration within 6-18 months of construction. The cause of this degradation is mainly due to combined exposure to repeated heat shocks from jet engine exhaust and spilled aviation oils (hydrocarbons). Surface degradation occurs in the form of disintegration of aggregates and cement paste into small pieces that pose severe risks of physical injury to maintenance crews or damage to an aircraft engine. Since coarse aggregates typically occupy 60-80% of the concrete volume, aggregates' thermal properties and microstructure should play a crucial role in the degrading mechanism. At high temperatures, concrete with lightweight aggregates is reported to have better performance compared to concrete with normal-weight aggregate. Thus, the present study carried out a detailed investigation of the mechanical and thermal performance of lightweight aggregate concrete exposed to the combined effects of high temperatures and hydrocarbon oils simultaneously. To replicate harsh airfield operating conditions, standard-sized concrete cylinders were exposed to elevated temperatures using an electric oven. Additionally, a mixture of equal parts of aircraft engine oil, hydraulic oil, and kerosene was applied before each exposure to high temperatures. To identify the resistance of different concrete with various lightweight coarse aggregates, pumice, perlite, lytag (sintered fly ash), and crushed brick were used as lightweight coarse aggregates in concrete. Also, basalt aggregate concrete was used as a reference. After curing, cylinders were tested for the ultimate strength. Later, after every 20 cyclic exposures, three cylinders from each aggregate type were tested for residual comprehensive strength, thermal, chemical, and microstructural (SEM) properties. Overall, concrete with crushed brick aggregate and lytag used in this study showed superior resistance to the simulated airfield conditions. The findings of this study will provide valuable insights to select an appropriate coarse aggregate type for military airfield pavement construction, aiming to effectively minimize surface spalling.
Keywords: lightweight aggregate; microstructure; residual strength; spalling; thermal properties.