Highly hydrophobic flax fabrics with durable properties were prepared using the "dip-coating" method for self-cleaning application. Flax fabrics were coated with a polysiloxane coating via a hydrosilylation reaction with a Karstedt catalyst at room temperature. The coated fabrics displayed highly and durable hydrophobic properties (contact angle and sliding angle of about 145° and 23°, respectively) with good self-cleaning ability for certain pollutants and excellent durability. Moreover, the influence of the coating process on the mechanical properties of fabrics was investigated. A decrease in E modulus and an increase in tensile stress at maximum force and elongation at maximum force has been observed. Furthermore, this influence of the coating process can be easily controlled by adjusting the proportion of curing agent in the treatment solution.
Keywords: PDMS; coating; flax fabric; hydrophobisation; hydrosilylation; self-cleaning.