Controlling the atomic arrangement of elemental atoms in intermetallic catalysts to govern their surface and subsurface properties is a crucial but challenging endeavor in electrocatalytic reactions. In hydrogen evolution reaction (HER), adjusting the d-band center of the conventional noble-metallic Pt by introducing Fe enables the optimization of catalytic performance. However, a notable gap exists in research on the effective transition from disordered Fe/Pt alloys to highly ordered intermetallic compounds (IMCs) such as FePt3 in the alkaline HER, hampering their broader application. In this study, a series of catalysts FePt3-xH (x = 5, 6, 7, 8 and 9) supported on carbon nanotubes (CNTs) were synthesized via a simple impregnation method, along with a range of heat treatment processes, including annealing in a reductive atmosphere, to regulate the order degree of the arrangement of Fe/Pt atoms within the FePt3 catalyst. By using advanced microscopy and spectroscopy techniques, we systematically explored the impact of the order degree of FePt3 in the HER. The as-prepared FePt3-8H exhibited notable HER catalytic activity with low overpotentials (η = 37 mV in 1.0 mol L-1 KOH) at j = 10 mA cm-2. The surface of the L12 FePt3-8H catalyst was demonstrated to be Pt-rich. The Pt on the surface was not easily oxidized due to the unique Fe/Pt coordination, resulting in significant enhancement of HER performance.
Keywords: Catalyst; Hydrogen evolution reaction; Intermetallic; Surface.
Copyright © 2024 Science China Press. Published by Elsevier B.V. All rights reserved.