The phase inversion tape casting has been widely used to fabricate open straight porous supports for solid oxide fuel cells (SOFCs), which can offer better gas transmission and minimize the concentration polarization. However, the overall weak strength of the macro-porous structure still limits the applications of these SOFCs. In this work, a novel SOFC supported by an ordered porous cathode membrane with a four-layer configuration containing a finger-like porous 3 mol% yttria- stabilized zirconia (3YSZ)-La0.8Sr0.2Co0.6Fe0.4O3-δ (LSCF) catalyst, porous 8 mol% yttria-stabilized zirconia (8YSZ)-LSCF catalyst, and dense 8YSZ porous 8YSZ-NiO catalyst is successfully prepared by the phase inversion tape casting, dip-coating, co-sintering, and impregnation process. The flexural strength of the open straight porous 3YSZ membrane is as high as 131.95 MPa, which meets the requirement for SOFCs. The cathode-supported single cell shows a peak power density of 540 mW cm-2 at 850 °C using H2 as the fuel. The degradation mechanism of the SOFC is investigated by the combination of microstructure characterization and distribution of relaxation times (DRT) analysis.
Keywords: DRT analysis; high strength; ordered cathode membrane; phase inversion; solid oxide fuel cell.