Carbon nanotubes (CNTs) filled natural rubber (NR) composites with various CNT contents at 0, 1, 2, 3, 4 and 5 phr were prepared by latex mixing method using glutaraldehyde as curing agent. This work aims to improve the electrical and mechanical properties of CNT filled NR vulcanizates. The CNT dispersion of NR composites was clarified using dispersion grader, optical microscopy and scanning electron microscopy. The electrical properties of NR composites in the existing of CNT networks were studied by following the well-known percolation theory. It was observed that the NR composites exhibited low percolation threshold at 0.98 phr of CNT. Moreover, a three-dimensional network formation of CNT in the NR composites was observed and it is indicated by the t-value of 1.67. The mechanical properties of NR composites in terms of modulus, tensile strength and hardness properties were increased upon the addition of CNT to the optimum mechanical properties at 1 phr of CNT. Therefore, the present work is found the novelty of the study that the conductive rubber latex film can be produced using GA as low-temperature curing agent which enhanced good electrical properties. Moreover, this work is found to be beneficial in case of conductive rubber latex film that requires high modulus at low strain. The additional advantage of this system is the curing process occurs at low-temperature using GA and it can be easily processed.
Keywords: Carbon nanotubes; Composites; Electrical conductivity; Glutaraldehyde; Natural rubber latex.
© 2024. The Author(s).