Ion-selective membrane has broad application in various fields, while the present solution-processed techniques can only prepare uniform membrane with microscale thickness. Herein, a high-quality polymer membrane with nanoscale thickness and uniformity is precisely prepared by controlling solution spreading and solvent evaporation stability/rate. With the arrayed capillaries, the stable spreading of polymer solution with volume of microliter induces the formation of solution film with micrometers thickness. Moreover, the fast increase of solution dynamic viscosity during solvent evaporation inhibits nonuniform Marangoni flow and capillary flow in solution film. Consequently, the uniform Nafion-Li membranes with ∼200 nm thickness are prepared, while their Li+ conductivity is 2 orders of magnitude higher than that of commercially Nafion-117 membrane. Taking lithium-sulfur battery as a model device, the cells (capacities of 8-10 mAh cm-2) can stably operate for 150 cycles at a S loading of 12 mg cm-2 and an electrolyte/sulfur ratio of ∼7.
Keywords: Marangoni flow; arrayed capillaries; capillary flow; ion-selective membrane.