There is a noticeable gap in the literature regarding research on halogen-substitution-regulated ferroelectric semiconductors featuring multiple phase transitions. Here, a new category of 1D perovskite ferroelectrics (DFP)2 SbX5 (DFP+ = 3,3-difluoropyrrolidium, X- = I- , Br- , abbreviated as I-1 and Br-2) with twophase transitions (PTs) is reported. The first low-temperature PT is a mmmFmm2 ferroelectric PT, while the high-temperature PT is a counterintuitive inverse temperature symmetry-breaking PT. By the substitution of iodine with bromine, the Curie temperature (Tc) significantly increases from 348 K of I-1 to 374 K of Br-2. Their ferroelectricity and pyroelectricity are improved (Ps value from 1.3 to 4.0 µC cm-2 , pe value from 0.2 to 0.48 µC cm-2 K-1 for I-1 and Br-2), while their optical bandgaps increased from 2.1 to 2.7 eV. A critical slowing down phenomenon is observed in the dielectric measurement of I-1 while Br-2 exhibits the ferroelastic domain. Structural and computational analyses elucidate that the order-disorder movement of cations and the distortion of the chain perovskite [SbX5 ]2- anions skeleton lead to PT. The semiconductor properties are determined by [SbX5 ]2- anions. The findings contribute to the development of ferroelectric semiconductors and materials with multiple PTs and provide materials for potential applications in the optoelectronic field.
Keywords: ferroelastic; ferroelectric semiconductors; halogen-substitution; inverse temperature symmetry breaking; multiple phase transition.
© 2024 Wiley-VCH GmbH.