The present study focuses on the multifunctional capabilities of carbon nanotube (CNT)-reinforced vitrimers. More specifically, the thermomechanical properties, the Joule effect heating capabilities, the electrical conductivity, the shape memory, and the chemical recycling capacity are explored as a function of the CNT content and the NH2/epoxy ratio. It is observed that the electrical conductivity increases with the CNT content due to a higher number of electrical pathways, while the effect of the NH2/epoxy ratio is not as prevalent. Moreover, the Tg of the material decreases when increasing the NH2/epoxy ratio due to the lower cross-link density, whereas the effect of the CNTs is more complex, in some cases promoting a steric hindrance. The results of Joule heating tests prove the suitability of the proposed materials for resistive heating, reaching average temperatures above 200 °C when applying 100 V for the most electrically conductive samples. Shape memory behavior shows an outstanding shape fixity ratio in every case (around 100%) and a higher shape recovery ratio (95% for the best-tested condition) when decreasing the NH2/epoxy ratio and increasing the CNT content, as both hinder the rearrangement of the dynamic bonds. Finally, the results of the recyclability tests show the ability to regain the nanoreinforcement for their further use. Therefore, from a multifunctional analysis, it can be stated that the proposed materials present promising properties for a wide range of applications, such as Anti-icing and De-icing Systems (ADIS), Joule heating devices for comfort or thermotherapy, or self-deployable structures, among others.
Keywords: Joule heating; chemical recycling; multifunctional materials; nanocomposites; shape memory.