Wood fibers (WFs) were treated at a fixed heat temperature (180 °C) for 2-6 h and added to a polylactic acid (PLA) matrix to produce wood-PLA composite (WPC) filaments. Additionally, the effects of the heat-treated WFs on the physicomechanical properties and impact strength of the WPC filaments and 3D-printed WPC parts using fused filament fabrication (FFF) were examined. The results revealed that heat-treated WFs caused an increase in crystallinity and a significant reduction in the number of pores on the failure cross section of the WPC filament, resulting in a higher tensile modulus and lower elongation at break. Additionally, the printed WPC parts with heat-treated WFs had higher tensile strength and lower water absorption compared to untreated WPC parts. However, most of the mechanical properties and impact strength of 3D-printed WPC parts were not significantly influenced by adding heat-treated WFs. As described above, at the fixed fiber addition amount, adding heat-treated WFs improved the dimensional stability of the WPC parts and it enabled a high retention ratio of mechanical properties and impact strength of the WPC parts.
Keywords: 3D printing; fused filament fabrication; heat treatment; physic and mechanical properties; wood fiber; wood–PLA composite (WPC).