Background: The dental profession is seeing a constant influx of new adhesive systems from manufacturers, each claiming to be more dependable than the last. This study assessed the bond strength and adhesive remnants of different light-cured adhesives used for bonding metal brackets to teeth.
Methods: 80 extracted maxillary premolars with the sound crown structure were acid etched and bonded with brackets on their buccal surfaces utilizing primer and light-cured adhesives into four equal groups, which are Transbond XT, Heliosit, Enlight, and Bracepaste. Shear bond strength (SBS) for de-bonding the brackets were evaluated with Instron- testing machine after 48 hours. The de-bonded samples' adhesive remnant index (ARI) scores were also measured.
Results: The maximum mean SBS was found for Transbond XT (12.91 ± 2.0 MPa), followed by Bracepaste (12.87 ± 1.59 MPa), Enlight (11.77 ± 1.87 MPa), and lowest for Heliosit (10.93 ± 1.71 MPa). According to the four point scale, adhesive remnant index (ARI), Transbond XT has the least adhesive residue left on the tooth, followed by Heliosit. Enlight and Bracepaste have a similar distribution of adhesive, with both having a maximum amount left.
Conclusion: It can be inferred that all groups involved demonstrated a satisfactory level of bond strength from a clinical perspective. Transbond XT is the preferred orthodontic adhesive over the other three adhesives due to its superior SBS and ARI properties.
Keywords: Adhesive Remnant Index; Bracket bonding adhesives; Light-cured adhesives; Orthodontic adhesives; Shear Bond Strength.