Bottom-gate thin-film transistors (TFTs) with n-type amorphous indium-gallium-zinc oxide (a-IGZO) active channels and indium-tin oxide (ITO) source/drain electrodes were fabricated. Then, an ultraviolet (UV) nanosecond pulsed laser with a wavelength of 355 nm was scanned to locally anneal the active channel at various laser powers. After laser annealing, negative shifts in the threshold voltages and enhanced on-currents were observed at laser powers ranging from 54 to 120 mW. The energy band gap and work function of a-IGZO extracted from the transmittance and ultraviolet photoelectron spectroscopy (UPS) measurement data confirm that different energy band structures for the ITO electrode/a-IGZO channel were established depending on the laser annealing conditions. Based on these observations, the electron injection mechanism from ITO electrodes to a-IGZO channels was analyzed. The results show that the selective laser annealing process can improve the electrical performance of the a-IGZO TFTs without any thermal damage to the substrate.
Keywords: ITO/IGZO energy band structure; UV pulsed laser annealing; a-IGZO TFT; selective annealing.