Tungsten is the most effective eco-friendly material used for radiation shielding in hospitals. However, despite its commendable density and shielding performance, tungsten faces challenges in miscibility with other materials because of its elevated melting point and strength. In this study, to protect medical personnel against scattered rays, which are indirect X-rays, a lightweight material was prepared by mixing graphite oxide material, considering its thinness and flexibility. Tungsten particles were evenly dispersed in the polymer, and nanofibers were prepared using this blended polymer solution via electrospinning. Concurrently, the process technology was explored to craft a thin film sheet and obtain a lead-like shielding effect. A spinning solution was prepared by mixing Fe3O4-rGO (FerGO) and tungsten. At 60 kVp, 0.1 mm was measured as 0.097 mmPb, at 80 kVp, 0.2 mm was measured as 0.196 mmPb, and at 100 kVp, 0.3 mm was measured as 0.279 mmPb, showing similar shielding performance to lead. As density directly affects the shielding effect, graphene oxide played an important role in increasing the density of the material from 1.941 g/cm3 to 2.302 g/cm3. Thus, this study provides an effective process for producing thin film sheets equivalent to lead.
Keywords: X-ray; graphene oxide; nanofiber; radiation; radiation exposure.