This study investigates the fracture behavior of glass fiber-reinforced plastic (GFRP) under various loading conditions using acoustic emission (AE) testing. Using fracture tests and time series analysis of AE signals, parameters such as b-value, improved b-value (Ib-value), and energy b-value (be-value) were examined to understand crack initiation, growth, and structural failure. The stress-strain curve revealed distinct responses during tensile and step loading, and time series analysis highlighted variations in amplitude, AE energy, and Kaiser and Felicity effects. Under tensile loading, the Ib-value exhibited a linear decrease, while step loading introduced complexities, including the Felicity effect. The be-value, incorporating energy considerations, fluctuated, providing insights into micro-cracks and macro-cracks. Statistical analysis demonstrated a consistent decrease in the be-value, emphasizing its potential for long-term monitoring. This study provides a comprehensive technique for assessing composite material fracture behavior, enhancing understanding for critical applications in hydrogen storage vessels and pressure pipes as well as advancing reliability and safety in industrial sectors.
Keywords: AE testing; GFRP; fracture behavior; structural integrity.