Crystal growth methods that do not require high temperatures are highly needed for the facile growth of oxide single crystals with melting points of several thousand degrees Celsius. This paper represents the first report of a method for the low-temperature growth of ruby crystals (chromium-doped Al2O3) at 750 °C, which is one-third of the conventionally required temperature (2050 °C). In solution-based crystal growth, the target crystal is grown at a temperature considerably lower than its melting point. However, conventional crystal growth processes involving solvent evaporation and cooling require high temperatures to completely liquefy the material, with previously reported solution growth temperatures of ≈1100 °C. Supersaturation based on the decomposition of crystal-solvent intermediates eliminates the need to completely liquefy the material, enabling low-temperature crystal growth. The combination of computational and experimental investigations helps determine the optimum conditions for low-temperature crystal growth. The proposed method is a novel green process that breaks the conventional frontiers of crystal growth while ensuring eco-friendliness and low energy consumption. In addition, its scope can potentially be expanded to the synthesis of various crystals and direct growth on substrates with low melting points.
Keywords: crystal–flux equilibrium; flux crystal growth; low‐temperature crystal growth; oxide single crystals; ruby crystals.
© 2024 Wiley‐VCH GmbH.