Herein, ZIF-8 inorganic particles with different sized reinforced poly (vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP) solid composite polymer electrolytes (PVDF-HFP/10%ZIF-8) were prepared via a facile blade-coating approach, and free-standing quasi solid-state composite electrolytes (PVDF-HFP/10%ZIF-8(0.6)/Plasticizer, abbreviated as PH/10%ZIF-8(0.6)/P), were further obtained through the introduction of plasticizer. Optimized PH/10%ZIF-8(0.6)/P exhibited a high ionic conductivity of 2.8 × 10-4 S cm-1 at 30 °C, and superior Li+ transfer number of 0.89 with an ultrathin thickness (26 µm). Therefore, PH/10%ZIF-8(0.6)/P could effectively inhibit the growth of lithium dendrites, and the assembled Li/LiFePO4 cell delivered good cycling stability with a capacity retention rate of 89.1% after 100 cycles at 0.5 C.
Keywords: composite polymer electrolytes; lithium metal batteries; poly (vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP); zeolitic imidazole framework-8 (ZIF-8).