Due to the growing interest in biopolymers, biosynthesizable and biodegradable polymers currently occupy a special place. Unfortunately, the properties of native biopolymers make them not good enough for use as substitutes for conventional polymers. Therefore, attempts are being made to modify their properties. In this work, in order to improve the properties of the poly(3-hydroxybutyrate) (P3HB) biopolymer, linear aliphatic polyurethane (PU) based on 1,4-butanediol (BD) and hexamethylene 1,6-diisocyanate (HDI) was used. The conducted studies on the effect of the amount of PU used (5, 10, 15 and 20 m/m%) showed an improvement in the thermal properties of the prepared polymer blends. As part of the tested mechanical properties of the new polymer blends, we noted the desired increase in the tensile strength, and the impact strength showed a decrease in hardness, in particular at the presence of 5 m/m% PU. Therefore, for further improvement, hybrid nanobiocomposites with 5 m/m% PU and organically modified montmorillonite (MMT) (Cloisite 30®B) were produced. The nanoadditive was used in a typical amount of 1-3 m/m%. It was found that the obtained nanobiocomposites containing the smallest amount of nanofillers, i.e., 1 m/m% Cloisite®30B, exhibited the best mechanical and thermal properties.
Keywords: modification; natural polyesters; structure-properties relationship.